IntroductionFormula:Epoxy resin (100%) 43% + benzyl alcohol 5% + CaCo3/43% + green pigment 4% +
Email: info@standard-groups.com
Formula:
Epoxy resin (100%) 43% + benzyl alcohol 5% + CaCo3/43% + green pigment 4% + additives 5%
Oil-based construction additives
| Category | Details |
|---|---|
| Product Type | High-performance industrial/commercial flooring system |
| Chemical Base | 100% solids epoxy resin + polyamine hardener |
| Key Applications | – Warehouses: Heavy traffic areas – Food Processing: Chemical resistant zones – Parking Decks: Abrasion-prone surfaces |
| Core Features | – Zero VOC: Environmentally compliant – Chemical Resistance: Withstands acids, oils, solvents – Thermal Shock Stability: -40°C to +120°C |
| Technical Data | – Pot Life: 30-45 mins @ 25°C – Cure Time: 24h walkable, 72h full cure – Abrasion Loss: <0.02g/1000 cycles (ASTM D4060) – Film Thickness: 150-300μm/coat |
| Performance | – Compression Strength: >80MPa – Adhesion: >2.5MPa (concrete failure) – Gloss: Semi-gloss (60°: 30-50 units) |
| Application | – Mixing Ratio: 2:1 by weight – Tools: Squeegee, roller – Substrate Prep: Shot blasting (Sa2.5) required |
| Safety | – Skin Contact: Immediate wash with soap – Eye Contact: Flush with water 15 mins – PPE: Full body suit, chemical goggles |
| Regulatory | Complies with LEED v4, REACH, FDA food contact regulations |
✔ 100% solids content for maximum durability
✔ Ultra-low VOC emission (<50g/L)
✔ Superior chemical and abrasion resistance
✔ Rapid cure time for minimal downtime
✔ Seamless, hygienic surface easy to clean
| Parameter | Component A | Component B | Mixed System |
|---|---|---|---|
| Base Material | Bisphenol-A epoxy | Modified polyamine | Crosslinked polymer |
| Solids Content | 100% | 100% | 100% |
| Viscosity (25°C) | 12.000-15.000 mPa·s | 800-1.200 mPa·s | 9.000-11.000 mPa·s |
| Mixing Ratio | – | – | 4:1 (A:B) by volume |
| Pot Life (25°C) | – | – | 40-60 minutes |
| Property | Test Method | Performance Data |
|---|---|---|
| Adhesion (pull-off) | ASTM D4541 | ≥5 MPa (concrete substrate) |
| Abrasion Resistance | ASTM D4060 | ≤50mg/1000 cycles |
| Chemical Resistance* | ASTM D1308 | Excellent (24h exposure) |
| Compressive Strength | ASTM D695 | ≥65 MPa |
| Cure Time (walk-on) | – | 12-16 hours |
| Full Cure | – | 7 days |
Resistant to acids (10%), alkalis (20%), oils, and most solvents
Application Guidelines
| Application Area | DFT per coat | Recommended Coats | Special Requirements |
|---|---|---|---|
| Light industrial | 0.3-0.5mm | 2 coats | Standard application |
| Heavy industrial | 0.5-0.8mm | 2-3 coats | Aggregate broadcast for wear |
| Food processing | 0.5-0.7mm | 2 coats + topcoat | NSF-approved formulation |
| Parking garages | 0.4-0.6mm | 2 coats | Anti-slip additives recommended |
| Clean rooms | 0.3-0.4mm | 2 coats | Conductive option available |
Disclaimer: The above content is for reference and communication only among industry insiders, and does not guarantee its accuracy or completeness. According to relevant laws and regulations and the regulations of this website, units or individuals who purchase related items should obtain valid qualifications and qualification conditions.
Company Phone
+86-21-6420 0566
Working hours
Monday to Friday
Mobile phone:
13816217984
Email:
info@qinsun-lab.com