Pure epoxy primer powder MT Plus -AL117N is a powder primer protective barrier designed to give enhanced corrosion protection of mild steel, hot dip galvanized steel and Zinc sprayed (gas flame/electrical deposition) and Aluminium. MT Plus is a pure epoxy primer showing a high cross-linking degree reinforced with barrier effect agents to provide the best barrier protection.
Pure epoxy primer powder MT Plus -AL117N must be over-coated with our powders or a Cromadex / Inernational PU liquid topcoat. It could be used as holding primer with a maximum waiting delay of 3 weeks.
Wide curing range, good mechanical properties, excellent edge coverage, good anti gassing properties, good over coating capacity.
| Chemical type | Thermosetting epoxy |
| Appearance | Smooth |
| Gloss level(60°) | Aspect may vary depending on curing conditions (green cure) |
| Color | Grey |
| Recommended Film Thickness (µm) | 60 – 80 µm |
| Density (g/cm3) | 1.5 ± 0.03 g/cm³ |
| Application | Electrostatic |
| Storage | Under dry, cool (≤ 30°C) conditions |
| Shelf life | At least 12 months from production date |
Surface preparation depends upon the metal, the type of surface, its conditions and the required performance.
| Substrate | Mechanical pretreatment | Chemical pretreatment |
| Mild steel | Grit Blasting Sa 2.5 in accordance with ISO NF EN 8501-1. Roughness: Rz 42 84 µm / Ra 6-12 µm. | Degreasing & phosphating (or equivalent) followed by passivation, DW rinsing and drying. |
| Cast steel | ||
| Electro Zinc steel | Sweeping with a maximum zinc layer thickness reduction of 5 to Degreasing & phosphating (or equivalent) followed by passivation, DW rinsing and drying. Hot dip galvanized steel Degreasing & phosphating / chromating followed by passivation. 10 µm depending on the initial zinc thickness. | |
| Hot dip galvanized steel | Degreasing & phosphating / chromating followed by passivation. | |
| Aluminium | Sweeping | Follow QUALICOAT (16th edition) recommendations for pre-treatment methods. |
| Zinc sprayed (gas flame/electrical deposition) | Grit Blasting Sa 3 in accordance with ISO NF EN 8501-1. Roughness: Rz 42 84 µm / Ra 6-12 µm | Banned |
MT Plus is suitable for corona electrostatic spraying.
| Recommended film thickness | 60-80 µm A good protection is linked with the recommended film thickness. |
| Recycling | Unused powder can be reclaimed using suitable equipment and recycled through the coating system, but a minimum of 70% new powder should be used. |
If you're ready to take the next step, Leave your message below and we’ll reply soon. 20+ years of chemical manufacturing & export experience, a partner you can trust.
Disclaimer: The above content is for reference and communication only among industry insiders, and does not guarantee its accuracy or completeness. According to relevant laws and regulations and the regulations of this website, units or individuals who purchase related items should obtain valid qualifications and qualification conditions.
Company Phone
+86-21-6420 0566
Working hours
Monday to Friday
Mobile phone:
13816217984
Email:
info@qinsun-lab.com